Dynamic mechanical moduli of residual softwood-filled polystyrene.

الناشر
Sultan Qaboos University
ميلادي
2009
اللغة
الأنجليزية
الملخص الإنجليزي
Residual softwood sawdust (RSS) was added to polystyrene (PS) that has molecular weight 280000 g/mol. The PS composite was prepared by melt mixing technique. The dynamic mechanical tests are carried out using ARES-rheometer (Rheometric Scientific, USA) in the dynamic mode and parallel plate geometry with diameter 25 mm. The measurements were performed at temperatures ranging from 140 to 240°C and frequencies varied from 0.1 to 100 rad/s at strain 1% and gap setting 2 mm. The dynamic mechanical properties in terms of complex modulus, G*, torque, compliance moduli, loss tangent and complex viscosity has been studied for fiber-filled PS composite. The viscoelastic properties of the filled and unfilled systems have been compared. These properties are found to be improved by the addition of RSS. The dynamic mechanical moduli and viscosity were found to rise with fiber loading.
ISSN
1726-6742
zcustom_txt_2
Abdel Goad, M. (2009). Dynamic mechanical moduli of residual softwood-filled polystyrene. The Journal of Engineering Research, 6 (1), 59-65.
الملخص العربي
تمت إضافة بقايا نشارة الخشب إلى البولي استيرين ذي الوزن الجزيئي العالي ( 28000 جم / مول). تم تحضير البولي استيرين المخلط بطريقة خلط المصهور. الخصائص الريولوجية تم تحديدها بواسطة جهاز الريموميتر عد درجات حرارة ما بين 140 إلى 240 درجة مئوية وتردد ما بين 1 إلى 100 لفة / ثانية. ومن البحث تبين أن الخصائص الريولوجية قد تحسنت كثيرا بإضافة هذه المخلفات الخشبية إلى البولي استيرين مما يمكن استخدامها على نطاق أوسع كمادة بلاستيكية.
قالب العنصر
مقالات الدوريات

مواد أخرى لنفس المؤلف

مقالات الدوريات
1
0
Abdel Goad, Mahmoud
Sultan Qaboos University
2009

مواد أخرى لنفس الموضوع

مقالات الدوريات
0
0
Singha, Tejeet
Sultan Qaboos University
2009
مقالات الدوريات
0
0
Aigbodion, V. S.
Sultan Qaboos University
2010